RT - Journal Article T1 - Laboratory evaluation of shear bond strength of porcelain repair methods JF - Caspian-J-Dent-Res YR - 2012 JO - Caspian-J-Dent-Res VO - 1 IS - 1 UR - http://cjdr.ir/article-1-55-en.html SP - 14 EP - 18 K1 - Shear bond strength K1 - Porcelain repair K1 - Resin cement AB - Introduction: Porcelain fracture is a relatively common problem in clinical dental practice. Various methods have been proposed for repairing porcelain fractures including direct composite resin repair or construction of a porcelain laminate veneer and its cementation with a resin cement. Evaluation of shear bond strength of porcelain repair methods was the purpose of this study. Methods: Twenty feldspathic porcelain discs (10 mm in diameter) were fabricated. The samples underwent air-born abrasion with an aluminum oxide and etching with HF, and were then ultrasonically cleaned and randomized into two groups: 1- repair with porcelain disc (7 mm in diameter) with light cure cement (Choice 2) and 2- repair with resin composite (Clearfil AP-X). We measured the shear bond strength of the samples by Zwick Roll at 0.5 mm/min crosshead speed. Results: The resin composite group had the highest shear bond strength (12.91 MPa). We found no significant differences between the choice and composite groups (p=0.970). Conclusions: Our findings indicate that resin composite yields acceptable shear bond strength to be used in porcelain repair. LA eng UL http://cjdr.ir/article-1-55-en.html M3 10.22088/cjdr.1.1.14 ER -